發表人	內容
上一篇主題下一篇主題
jules 資深會員註冊時間: Sep 15, 2004 文章: 576 來自: 秀水	發表於: 星期六 2005-02-26 20:47 在下找到了三種950的platinum（95%的鉑，加上5%的其它金屬）資料，第一種是鉑銥合金，硬度只有80 vickers，軟到不行。第二種是鉑釕合金，硬度135vickers，第三種是鉑鈷合金，硬度也是135vickers（但是這種合金因為含鈷，所以有磁性，而且顏色偏藍，通常要在外表鍍上一層銠，想也知道不適合製表殼）而一般18k的合金表殼，硬度約從135到155vickers 之間。所以950鉑殼並沒有比較硬，而純鉑的硬度約80 vickers，是比純金硬，但仍無法製表殼。請不吝指正回頂端

spikegifted 進階會員註冊時間: Dec 30, 2004 文章: 280 來自: London, UK	發表於: 星期六 2005-02-26 23:23 All this talk doesn't really address the real issue: gold as a metal is relatively soft and highly ductile, which means that if you use it as case material for a watch and you wear it for any period of time, you're going to have scratches on it. For most high quality watches, the gold used in the material is going to be somewhere between 18k to 'solid' gold (read: 22k), so even as an alloy, with such high gold content means that the resultant material is still relatively soft. (See physical properties of gold.) 回頂端

AlainS 資深會員註冊時間: Oct 05, 2004 文章: 821 來自: Singapore	發表於: 星期一 2005-02-28 12:59 由於其稀有性,及高溶點(鉑金溶點非常高,高達1773'C)因而不易加工,所以以鉑金製成的錶都比白金或黃金貴很多. 但由於鉑金950其純度高,所以硬度也相對較低,故比一般以白金750(18K)製成的錶殼易刮傷. 珠寶首飾會使用鉑金900來製作結婚戒指,原因是鉑金比白金或黃金稀少,也更不易氧化.因此象徵永恆回頂端

spikegifted 進階會員註冊時間: Dec 30, 2004 文章: 280 來自: London, UK	發表於: 星期二 2005-03-01 05:16 Good point, AlainS! I forgot that platinum and white gold are the same words in Chinese... Of course, platinum is a lot stronger than gold or even gold alloies. However, it is still not as tough as say stainless steel... 回頂端

jeffchang 中級會員註冊時間: Jan 03, 2005 文章: 113 來自: 台灣	發表於: 星期二 2005-03-01 09:29 Thank you all, I learned a lot during this forum. 回頂端

AlainS 資深會員註冊時間: Oct 05, 2004 文章: 821 來自: Singapore	發表於: 星期二 2005-03-01 09:46 回頂端

AlainS 資深會員註冊時間: Oct 05, 2004 文章: 821 來自: Singapore	發表於: 星期二 2005-03-01 14:58 忘了一件事,platinum與gold是不同的化學元素,所以有些錶店會翻譯platinum950為950純白金是錯誤的.platinum中文翻譯為鉑. 回頂端